Peaks of anatase were not observed at 750℃.

时已经观察不到锐钛矿型的衍射峰。

Pure anatase can be obtained without being sintered by controlling experimental conditions.

通过控制实验条件，可以得到单一的锐钛矿相TiO2纳米晶。

With an increase in the flame power, the content of anatase TiO2 is decreased and grain size of TiO2 is increased.

减小液料热喷涂功率，有利于提高锐钛矿相含量、减小晶粒尺寸。

Anatase solution and inorganic agglutinant such as low-temperature glaze and silica gel were used to prepare antibacterial ceramic tile in the third chapter.

第三章研究了利用锐钛矿型二氧化钛浆料及无机黏结剂如低温釉和硅胶制备杀菌陶瓷；

Why add phosphoric acid in anatase titanium dioxide?

阐述了在生产锐钛型钛白粉颜料中,加入磷酸的目的、量、钛白粉的影响,以及加入磷酸的方法.

In the condition of lower applied voltage, the film is mainly composed of anatase phase.

随着处理电压的升高，氧化膜中金红石相的相对含量增加；

TiO 2 film with anatase crystallite and porous structure was available by controlling the preparation conditions.

通过控制制备条件得到的TiO2薄膜具有锐钛晶型和多孔性结构.

At the same time the relative content of anatase and rutile can be determined by the intensity of main peak in TiO2 XRD patterns.

同时通过XRD对主峰衍射强度的测定可以确定TiO2重量中各晶型的含量。

The preparation method and the crystalline transformation conditions of titania mica pearlescent pigments coated with anatase and rutile were investigated.

本文着重研究了涂层为锐钛和金红石两种晶型的云母钛珠光颜料的制备方法，晶型转化的影响因素及各自的性能特征；